| Tabela referencyjna: Tabela przeliczeniowa twardości stali – wszystkie wartości są przybliżone. | ||||
| Twardość Brinella | Rockwella | Rockwella | Vickers | N/mm² |
| HB | HRC | HRB | HV | |
| 800 HB | 72 HRC | – | – | – |
| 780 HB | 71 HRC | – | – | – |
| 760 HB | 70 HRC | – | – | – |
| 752 HB | 69 HRC | – | – | – |
| 745 HB | 68 HRC | – | – | – |
| 746 HB | 67 HRC | – | – | – |
| 735 HB | 66 HRC | – | – | – |
| 711 HB | 65 HRC | – | – | – |
| 695 HB | 64 HRC | – | – | – |
| 681 HB | 63 HRC | – | – | – |
| 658 HB | 62 HRC | – | – | – |
| 642 HB | 61 HRC | – | – | – |
| 627 HB | 60 HRC | – | – | – |
| 613 HB | 59 HRC | – | – | – |
| 601 HB | 58 HRC | – | 746 HV | – |
| 592 HB | 57 HRC | – | 727 HV | – |
| 572 HB | 56 HRC | – | 694 HV | – |
| 552 HB | 55 HRC | – | 649 HV | – |
| 534 HB | 54 HRC | 120 HRB | 589 HV | – |
| 513 HB | 53 HRC | 119 HRB | 567 HV | – |
| 504 HB | 52 HRC | 118 HRB | 549 HV | – |
| 486 HB | 51 HRC | 118 HRB | 531 HV | – |
| 469 HB | 50 HRC | 117 HRB | 505 HV | – |
| 468 HB | 49 HRC | 117 HRB | 497 HV | – |
| 456 HB | 48 HRC | 116 HRB | 490 HV | 1569 N/mm² |
| 445 HB | 47 HRC | 115 HRB | 474 HV | 1520 N/mm² |
| 430 HB | 46 HRC | 115 HRB | 458 HV | 1471 N/mm² |
| 419 HB | 45 HRC | 114 HRB | 448 HV | 1447 N/mm² |
| 415 HB | 44 HRC | 114 HRB | 438 HV | 1422 N/mm² |
| 402 HB | 43 HRC | 114 HRB | 424 HV | 1390 N/mm² |
| 388 HB | 42 HRC | 113 HRB | 406 HV | 1363 N/mm² |
| 375 HB | 41 HRC | 112 HRB | 393 HV | 1314 N/mm² |
| 373 HB | 40 HRC | 111 HRB | 388 HV | 1265 N/mm² |
| 360 HB | 39 HRC | 111 HRB | 376 HV | 1236 N/mm² |
| 348 HB | 38 HRC | 110 HRB | 361 HV | 1187 N/mm² |
| 341 HB | 37 HRC | 109 HRB | 351 HV | 1157 N/mm² |
| 331 HB | 36 HRC | 109 HRB | 342 HV | 1118 N/mm² |
| 322 HB | 35 HRC | 108 HRB | 332 HV | 1089 N/mm² |
| 314 HB | 34 HRC | 108 HRB | 320 HV | 1049 N/mm² |
| 308 HB | 33 HRC | 107 HRB | 311 HV | 1035 N/mm² |
| 300 HB | 32 HRC | 107 HRB | 303 HV | 1020 N/mm² |
| 290 HB | 31 HRC | 106 HRB | 292 HV | 990 N/mm² |
| 277 HB | 30 HRC | 105 HRB | 285 HV | 971 N/mm² |
| 271 HB | 29 HRC | 104 HRB | 277 HV | 941 N/mm² |
| 264 HB | 28 HRC | 103 HRB | 271 HV | 892 N/mm² |
| 262 HB | 27 HRC | 103 HRB | 262 HV | 880 N/mm² |
| 255 HB | 26 HRC | 102 HRB | 258 HV | 870 N/mm² |
| 250 HB | 25 HRC | 101 HRB | 255 HV | 853 N/mm² |
| 245 HB | 24 HRC | 100 HRB | 252 HV | 838 N/mm² |
| 240 HB | 23 HRC | 100 HRB | 247 HV | 824 N/mm² |
| 233 HB | 22 HRC | 99 HRB | 241 HV | 794 N/mm² |
| 229 HB | 21 HRC | 98 HRB | 235 HV | 775 N/mm² |
| 223 HB | 20 HRC | 97 HRB | 227 HV | 755 N/mm² |
| 216 HB | 19 HRC | 96 HRB | 222 HV | 716 N/mm² |
| 212 HB | 18 HRC | 95 HRB | 218 HV | 706 N/mm² |
| 208 HB | 17 HRC | 95 HRB | 210 HV | 696 N/mm² |
| 203 HB | 16 HRC | 94 HRB | 201 HV | 680 N/mm² |
| 199 HB | 15 HRC | 93 HRB | 199 HV | 667 N/mm² |
| 191 HB | 14 HRC | 92 HRB | 197 HV | 657 N/mm² |
| 190 HB | 13 HRC | 92 HRB | 186 HV | 648 N/mm² |
| 186 HB | 12 HRC | 91 HRB | 184 HV | 637 N/mm² |
| 183 HB | 11 HRC | 90 HRB | 183 HV | 617 N/mm² |
| 180 HB | 10 HRC | 89 HRB | 180 HV | 608 N/mm² |
| 175 HB | 9 HRC | 88 HRB | 178 HV | 685 N/mm² |
| 170 HB | 7 HRC | 87 HRB | 175 HV | 559 N/mm² |
| 167 HB | 6 HRC | 86 HRB | 172 HV | 555 N/mm² |
| 166 HB | 5 HRC | 86 HRB | 168 HV | 549 N/mm² |
| 163 HB | 4 HRC | 85 HRB | 162 HV | 539 N/mm² |
| 160 HB | 3 HRC | 84 HRB | 160 HV | 535 N/mm² |
| 156 HB | 2 HRC | 83 HRB | 158 HV | 530 N/mm² |
| 154 HB | 1 HRC | 82 HRB | 152 HV | 515 N/mm² |
| 149 HB | – | 81 HRB | 149 HV | 500 N/mm² |
| 147 HB | – | 80 HRB | 147 HV | 490 N/mm² |
| 143 HB | – | 79 HRB | 146 HV | 482 N/mm² |
| 141 HB | – | 78 HRB | 144 HV | 481 N/mm² |
| 139 HB | – | 77 HRB | 142 HV | 480 N/mm² |
| 137 HB | – | 76 HRB | 140 HV | 475 N/mm² |
| 135 HB | – | 75 HRB | 137 HV | 467 N/mm² |
| 131 HB | – | 74 HRB | 134 HV | 461 N/mm² |
| 127 HB | – | 72 HRB | 129 HV | 451 N/mm² |
| 121 HB | – | 70 HRB | 127 HV | 431 N/mm² |
| 116 HB | – | 68 HRB | 124 HV | 422 N/mm² |
| 114 HB | – | 67 HRB | 121 HV | 412 N/mm² |
| 111 HB | – | 66 HRB | 118 HV | 402 N/mm² |
| 107 HB | – | 64 HRB | 115 HV | 382 N/mm² |
| 105 HB | – | 62 HRB | 112 HV | 378 N/mm² |
| 103 HB | – | 61 HRB | 108 HV | 373 N/mm² |
| 95 HB | – | 56 HRB | 104 HV | – |
| 90 HB | – | 52 HRB | 95 HV | – |
| 81 HB | – | 41 HRB | 85 HV | – |
| 76 HB | – | 37 HRB | 80 HV | – |
| Twardość Brinella | Rockwella | Rockwella | Vickers | N/mm² |
| HB | HRC | HRB | HV | |
| 3000kg | 150kg | 100kg | Diamentowa Piramida | Wytrzymałość na rozciąganie (w przybliżeniu) |
| Kula 10mm | Brale | Kula 1/16″ | 120kg | |
| Tabela referencyjna: Tabela konwersji twardości stali | ||||
| Ponieważ różne rodzaje testów twardości nie mierzą tej samej kombinacji właściwości materiału, przeliczenie z jednej skali twardości na drugą jest procesem tylko przybliżonym. Ze względu na szeroki zakres zmienności między różnymi materiałami nie jest możliwe określenie granic ufności dla błędów w stosowaniu wykresu konwersji. | ||||
- tiz@tiz.pl
- Ulica Kocjana 1-U4, 01-473 Warszawa, Polska
- 22 423-33-14/15
Ostatnie wpisy
Jak uczyli się i żyli studenci średniowiecznych uniwersytetów?
Bolonia, na przykład, miała około 500 do 1500 studentów w XIII wieku, jest to dużo jak na współczesne małe miasto,
Pierwsze uniwersytety
Pierwszy europejski uniwersytet znajdował się w Bolonii. Była to gildia dorosłych uczniów, którzy chcieli zdobyć dodatkową wiedzę. Studenci sami wybierali
Energia wodorowa w UE
Temat energii wodorowej nie pojawił się ani dziś, ani wczoraj. Po raz pierwszy tak duży wzrost zainteresowania nią nastąpił w
Podziel się tym wpisem ze swoimi znajomymi
Share on facebook
Share on twitter
Share on linkedin
Share on whatsapp
Share on pinterest
Share on email